Zig-zag trench structure to prevent aspect ratio trapping defect escape

ABSTRACT

A semiconductor structure including: trench-defining layer; an epitaxial layer; and a set of defect-blocking member(s). The trench-defining layer includes a trench surface which defines an elongated interior space called the “trench.” The epitaxial layer is grown epitaxially in the interior space of the trench. Each defect blocking member of the set of defect blocking members: (i) extends from a portion of trench surface into the interior space of the trench; and (ii) is located below a top surface of the epitaxial layer. The defect blocking member(s) are designed to arrest the propagation of generally-longitudinal defects in the epitaxial layer, as it is grown, where the generally-longitudinal defects are defects that propagate at least generally in the elongation direction of the trench.

BACKGROUND OF THE INVENTION

The present invention relates generally to the field of field-effect transistors (FETs, NFETs, PFETs), and more particularly to trench structures, for FETs, with relatively large lattice mismatch in their constituent materials.

III-V semiconductors have larger lattice constants than silicon, so integrating them on silicon is challenging. Methods for integrating III-V semiconductors on silicon have included blanket III-V growth and aspect ratio trapping (ART). Many semiconductor materials, such as silicon (Si) have, at the atomic level, a lattice structure. When two different semiconductor materials are intermingled, or placed in close proximity, it is generally better if the lattice constants of the two semiconductor materials are compatible, as such compatibility is understood by those of skill in the art. Aspect ratio trapping is an effective technique to trap threading dislocations, thereby reducing the dislocation density of lattice mismatched materials grown on silicon. The ART technique can be performed using thinner III-V layers. Trenches are employed for trapping misfit threading dislocations by stopping their propagation. The III-V material is grown in narrow trenches. The dislocations end at the trench walls, but fairly high defect densities up to 100,000,000/cm² can still be observed. The present invention shows a structure to further reduce those defect densities. The performance of devices fabricated using dissimilar semiconductor materials can be materially affected by defects that cause abrupt changes in electrical and/or optical properties. Adverse effects due to misfit defects and threading dislocations should be minimized or avoided in the fabrication of electronic devices incorporating such semiconductor materials.

NFETs made using silicon and III-V compounds are known, best known is InGaAs. III-V materials are chemical compounds with at least one group III (IUPAC (International Union of Pure and Applied Chemistry) group 13) element and at least one group V element (IUPAC group 15). NFETs are considered a high performance option for future technology nodes (7 nm (nano meters) and beyond). Co-integration of III-V with silicon deals with a known challenge due to the high lattice mismatch of some III-V semiconductor materials and silicon (and germanium (Ge) and silicon-germanium (SiGe)). Aspect ratio trapping (ART) is a known technique that can be used to counter and/or overcome lattice mismatch issues. In currently conventional ART structures, trenches with parallel sidewalls are formed.

NFETs conventionally include trench structures that use III-V semiconductor material, with high electron mobility, such as GaAs (gallium arsenide), InGaAs (indium gallium arsenide) or InAs (indium arsenide). Some conventional PFETs also include trench structures that use III-V semiconductor material, like InGaSb (indium gallium antimonide), which has a high hole mobility.

SUMMARY

According to an aspect of the present invention, there is a semiconductor structure including: (i) a trench-defining layer; (ii) an epitaxial layer; and (iii) a set of defect-blocking member(s) including at least one defect-blocking member. The epitaxial layer is formed by epitaxial growth. The trench-defining layer includes a trench surface which defines an elongated trench interior space. Each defect-blocking member of the set of defect-blocking members extends from the trench surface into the trench interior space. The epitaxial layer is located in the portions of the trench interior space not occupied by the set of defect-blocking member(s).

According to a further aspect of the present invention, a method of at least partially fabricating a semiconductor device includes the following steps (not necessarily in the following order): (i) providing an initial sub-assembly including a trench-defining layer having a top surface; (ii) refining the initial sub-assembly into a first trench-cut intermediate sub-assembly by removing material to form an upper tier of a trench extending downward from the top surface of the trench-defining layer, the upper tier of the trench including two lateral trench surfaces and a bottom trench surface; and (iii) refining the first trench-cut intermediate sub-assembly into a second trench-cut intermediate sub-assembly by selectively removing material in a downwards direction starting from the bottom surface of the trench to form a lower tier of the trench, with the selective removal of material leaving at least a first defect blocking member in the lower tier of the trench.

According to a further aspect of the present invention, a field-effect transistor (FET) device includes: (i) a FET components set including a first gate and a first contact; (ii) trench-defining layer; (iii) an epitaxial layer; and (iv) a set of defect-blocking member(s) including at least one defect-blocking member. The epitaxial layer is formed by epitaxial growth. The trench-defining layer includes a trench surface which defines an elongated trench interior space. Each defect-blocking member of the set of defect-blocking members extends from the trench surface into the trench interior space. The epitaxial layer is located in the portions of the trench interior space not occupied by the set of defect-blocking member(s). The FET components set are located at least partially on top of a top surface of the epitaxial layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an orthographic top view of a first embodiment of a semiconductor structure according to the present invention as it is undergoing fabrication;

FIG. 2 is a transverse cross-sectional view (specifically a cross-sectional slice view showing only material present in the cutting plane shown on FIG. 1) of the first embodiment semiconductor structure under fabrication;

FIG. 3 is a longitudinal cross-sectional view of a portion of the first embodiment semiconductor structure under fabrication;

FIG. 4 is another transverse cross-sectional view (specifically a cross-sectional slice view showing only material present in the cutting plane shown on FIG. 1) of the first embodiment semiconductor structure under fabrication;

FIG. 5 is an orthographic top view of a first embodiment of a semiconductor structure according to the present invention as it is undergoing further fabrication;

FIG. 6 is a transverse cross-sectional view (specifically a cross-sectional slice view showing only material present in the cutting plane shown on FIG. 5) of the first embodiment semiconductor structure as it is undergoing further fabrication;

FIG. 7 is a longitudinal cross-sectional view of a portion of the first embodiment semiconductor structure as it is undergoing further fabrication;

FIG. 8 is another transverse cross-sectional view (specifically a cross-sectional slice view showing only material present in the cutting plane shown on FIG. 5) of the first embodiment semiconductor structure as it is undergoing further fabrication;

FIG. 9 is an orthographic top view of a first embodiment of a semiconductor structure according to the present invention as it is undergoing still further fabrication;

FIG. 10 is a transverse cross-sectional view (specifically a cross-sectional slice view showing only material present in the cutting plane shown on FIG. 9) of the first embodiment semiconductor structure as it is undergoing still further fabrication;

FIG. 11 is a longitudinal cross-sectional view of a portion of the first embodiment semiconductor structure as it is undergoing still further fabrication;

FIG. 12 is another transverse cross-sectional view (specifically a cross-sectional slice view showing only material present in the cutting plane shown on FIG. 9) of the first embodiment semiconductor structure as it is undergoing still further fabrication;

FIG. 13 is a perspective view of the first embodiment semiconductor structure as it exists as the FIG. 1 stage of fabrication;

FIG. 14 is an orthographic top view of a second embodiment of a semiconductor structure according to the present invention as it is undergoing fabrication;

FIG. 15 is an orthographic top view of a third embodiment of a semiconductor structure according to the present invention as it is undergoing fabrication;

FIG. 16 is an orthographic top view of a fourth embodiment of a semiconductor structure according to the present invention as it is undergoing fabrication;

FIG. 17 is an orthographic top view of a fifth embodiment of a semiconductor structure according to the present invention as it is undergoing fabrication; and

FIG. 18 is an orthographic top view of a sixth embodiment of a semiconductor structure according to the present invention as it is undergoing fabrication.

DETAILED DESCRIPTION

Some embodiments of the present invention are directed to techniques for addressing defect issues in the manufacture of devices employing semiconductor materials having dissimilar properties, such as dissimilar lattice constants.

Some embodiments of the present invention recognize the following facts, potential problems and/or potential areas for improvement with respect to the current state of the art: the use of parallel trenches in ART style FETs leads to the problem of defects parallel to the direction of elongation of the trench “escaping.” More specifically, the recognized risk is that the semiconductor material used to fill the trench can, during its epitaxial growth inside the interior space of the trench, develop defects that propagate in a direction that is parallel, or at least generally parallel, to the direction of elongation of the trench. While the side walls that help define the trench will arrest defect propagation in a direction transverse, or at least generally transverse, to the trench, in conventional FETs, a defect running generally in the longitudinal direction can propagate as the epitaxial semiconductor material layer is grown up inside the interior space of the trench.

Some embodiments of the present invention are directed to a semiconductor device including: trench-defining layer; an epitaxial layer; and a set of defect-blocking member(s). The trench-defining layer includes a trench surface which defines an interior space (sometimes herein called the trench). The trench-defining layer may include a base sub-layer and a lateral-wall sub-layer, and these sub-layers may be made of different materials. The epitaxial layer is grown epitaxially in the interior space of the trench. Each defect blocking member of the set of defect blocking member(s): (i) extends from a portion of trench surface into the interior space of the trench; and (ii) is located below a top surface of the epitaxial layer. The defect blocking member(s) are designed to arrest the propagation of generally-longitudinal defects in the epitaxial layer, as it is grown, where the generally-longitudinal defects are defects that propagate at least generally in the elongation direction of the trench. The entire trench can be patterned with fins, if desired.

FIGS. 1 to 13 show semiconductor device 100, 200, 300 as it exists at three stages of the fabrication process, specifically: (i) trench-cut intermediate sub-assembly 100 (see FIGS. 1 to 4 and 13); (ii) epitaxially-grown intermediate sub-assembly 200 (see FIGS. 5 to 8); and (iii) planarized intermediate sub-assembly 300 (see FIGS. 9 and 10). Before going into a detailed discussion, the reader's attention is first drawn to FIG. 13, which is a perspective view that shows defect-blocking members 107, 108, 110 in an easy to understand way. These defect blocking members block propagation of defects that run generally in the elongation direction E of trench 106.

As shown in FIGS. 1 to 4 and 13, trench-cut intermediate sub-assembly 100 includes: lateral wall sub-layer 102 (including first lateral wall portion 102a and second lateral wall portion 102b, first defect-blocking member 107, second defect-blocking member 108, third defect-blocking member 110 and fourth defect-blocking member 112); base sub-layer 104; and trench interior space (also called, more simply, “trench”) 106 (including upper trench portion 106 a and lower trench portion 106 b). Taken together, lateral sub-wall layer 102 and base sub-layer 104 make up an “aspect ratio trapping trench-defining layer” 102, 104. The interior space of trench 106 is defined by the trench-facing surfaces of sub-layer 102 and sub-layer 104 (as is best seen with reference to the perspective view of FIG. 13).

In this example, base sub-layer 104 is made of silicon substrate material and is 875 micrometer thick based on use for a 300 mm (millimeter) wafer (825 micrometer for a 200 mm silicon wafer). When the FET device is finished, the role of base sub-layer 104 is to hold the device in place—it serves as the base of an integrated circuit chip.

In this example, lateral wall sub-layer 102 is made of material suitable for defining an aspect ratio trapping trench (such as dielectric materials, like silicon oxide or nitride), and has a thickness appropriate to an aspect ratio trapping trench.

In this example, defect-blocking members 107, 108, 110, 112 are formed to be of the same material and unitary with lateral wall sub-layer 102. More specifically, trench 106 and defect-blocking members 107, 108, 110, 112 are formed and shaped by performing reactive ion etching on a flat, planar layer of the lateral wall material. Even more specifically, in order to form the trench and defect-blocking members of trench-cut intermediate sub-assembly 100: (i) the top surface is masked off except for an elongated and straight path where upper portion (or tier) 106 a of trench 106 will be removed; (ii) upper tier 106 a of trench 106 is formed by reactive ion etching (in this example, upper tier 106 a has a depth equal to about half of the total depth of trench 106); (iii) the top surface of the lateral wall material that is inside the trench is further selectively masked off (that is, masks are placed according to the plan view footprints of the defect-members to be formed); (iv) lower tier 106 a of trench 106 is formed by further reactive ion etching; and (v) the masking is removed to yield trench-cut intermediate sub-assembly 100.

In this example, the lower tier 106 b of trench 106 can be described as “zig-zag” because of the pattern formed by the defect blocking members.

As shown in FIGS. 5 to 8, epitaxially-grown intermediate sub-assembly 200 includes: lateral wall sub-layer 102; base sub-layer 104; defect-blocking members 108, 110; and epitaxial layer 202.

In this example, epitaxial layer 202 is made of a III-V semiconductor material, specifically GaAs. Alternatively, any material (now known or to be developed in the future) to which an aspect ratio trapping trench is applicable could be used (for example, other III-V semiconductor materials such as, InGaAs, GaAs, or InGaAs. Epitaxial layer 202 is epitaxially grown to an extent that epitaxial layer 202 substantially fills trench 106, at least up to the height of lateral walls 102 a, b. When the aspect ratio trapping trench structure is finished, the epitaxial layer can be used in fabricating semiconductor devices, such as NFETs and PFETs, as will be understood by those of skill in the art. The epitaxial growth techniques used to form epitaxial layer 202 may be any epitaxial growth of semiconductor material techniques currently conventional or to be developed in the future. However, the epitaxial growth of this embodiment of the present invention is less subject to large scale defects than conventional epitaxial growths, grown in epitaxial aspect ratio trapping trenches having no defect blocking members.

As shown in FIGS. 6, 7 and 8, the top surface of epitaxial layer 202 is not necessarily flat in epitaxially-grown intermediate sub-assembly 200, and this is due in part to the irregularities of the trench defining surface caused by defect-blocking members 107, 108, 110, 112. However, in other (perhaps more preferred) embodiments, the epitaxial layer is grown so that it: (i) in some portions (for example, near the trench walls), reaches at least the level of the top plane of the trench; and (ii) in some portions (for example, away from the trench walls), extends above the top plane of the trench. In this embodiment, epitaxial layer 202 grows only bottom up from base sub-layer layer 104 and does not grow from aspect ratio trapping trench-defining sub-layer 102 (because sub-layer 102 is made from dielectric material in this example).

The role of defect-blocking member(s) set 107, 108, 110, 112 will now be discussed. As epitaxial layer 202 is epitaxially grown within the interior space of lower portion 106 b of trench 106, any longitudinally-running defects caused by lattice mismatching will be stopped in their longitudinal direction propagation (that is, trench direction propagation) by the defect blocking members. This means that the defect propagation to the surface will be blocked, and a relatively defect-free surface will be accomplished so that performance of a semiconductor device made on this surface is not made less favorable by the defects (for example, defects caused by lattice mismatch between the materials of base sub-layer 104 and epitaxial layer 202).

As shown in FIGS. 9 to 12, planarized intermediate sub-assembly 300 includes: lateral wall sub-layer 102; base sub-layer 104; defect-blocking member 110; and epitaxial layer 202. In order to refine epitaxially-grown sub-assembly 200 into planarized sub-assembly, material is removed in a top down manner from sub-assembly 200, by chemical-mechanical planarization, until planarized intermediate sub-assembly 300 is obtained. Although FIG. 8 shows an example, where the epitaxial layer has not grown all the way to the top of the trench walls, at least some embodiments of the present invention: (i) grow the epitaxial layer above the height of the sidewalls; (ii) then CMP (chemical-mechanical-planarize) the structure using the top surface of the lateral wall sub-layer as a stopping plane for the downward removal of material by CMP; and (iii) resulting a structure where the top surface of the lateral wall sub-layer and the top surface of the epitaxial layer are co-planar. A device (for example, an NFET can later be built on the planarized top surface of epitaxial layer 202. To put it another way, epitaxial layer 202 may serve as a substrate for later building a semiconductor device.

FIGS. 14 to 18 respectively show plan views, at the trench-cut intermediate sub-assembly stage, for a variety of alternative embodiments as follows: (i) FIG. 14 shows sub-assembly 500 with longitudinally-aligned defect blocking members; (ii) FIG. 15 shows sub-assembly 600 with defect blocking members that extend from the base of the trench, but do not extend from the lateral walls of the trench; (iii) FIG. 16 shows sub-assembly 700 with sinusoidal defect-blocking members; (iv) FIG. 17 shows sub-assembly 800 with saw tooth profile defect-blocking members; and (v) FIG. 18 shows sub-assembly 900 with defect-blocking members extending from one lateral trench wall, but not the other lateral trench wall.

Further with respect to sub-assembly 700 of FIG. 16, lines L1 and L2 show two examples of potential, generally-longitudinal defect paths. L1 is close to parallel to the lateral side walls of the trench, while L2 is only generally parallel to the side walls of the trench. The fact that these potential defect paths pass through the sinusoidal defect blocking members shows how the defect-blocking members can stop defect growth, during the growing of the epitaxial layer. Similarly, potential defect path L6 as shown in FIG. 14.

Further with respect to sub-assemblies 500, 600 and 900 respectively of FIGS. 14, 15 and 18, lines L3, L4 and L5 show examples of potential, generally-longitudinal defect paths that would not be stopped in their propagation by the defect-blocking members. This is a potential relative disadvantage of these embodiments, but they are included here to help demonstrate the full potential scope of the present invention.

The descriptions of the various embodiments of the present invention have been presented for purposes of illustration, but are not intended to be exhaustive or limited to the embodiments disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the invention. The terminology used herein was chosen to best explain the principles of the embodiment, the practical application or technical improvement over technologies found in the marketplace, or to enable others of ordinary skill in the art to understand the embodiments disclosed herein.

The following paragraphs set forth some definitions for certain words or terms for purposes of understanding and/or interpreting this document.

Present invention: should not be taken as an absolute indication that the subject matter described by the term “present invention” is covered by either the claims as they are filed, or by the claims that may eventually issue after patent prosecution; while the term “present invention” is used to help the reader to get a general feel for which disclosures herein are believed to potentially be new, this understanding, as indicated by use of the term “present invention,” is tentative and provisional and subject to change over the course of patent prosecution as relevant information is developed and as the claims are potentially amended.

Embodiment: see definition of “present invention” above—similar cautions apply to the term “embodiment.”

and/or: inclusive or; for example, A, B “and/or” C means that at least one of A or B or C is true and applicable. 

1. A semiconductor structure comprising: a trench-defining layer; an epitaxial layer; and a set of defect-blocking member(s) including at least one defect-blocking member; wherein: the epitaxial layer is formed by epitaxial growth; the trench-defining layer includes a trench surface which defines an elongated trench interior space; each defect-blocking member of the set of defect-blocking members extends from the trench surface into the trench interior space; and the epitaxial layer is located in the portions of the trench interior space not occupied by the set of defect-blocking member(s).
 2. The semiconductor structure of claim 1 wherein the set of defect blocking member(s) are sized, shaped and/or located to prevent lattice mismatch defects from propagating through the epitaxial layer generally in the direction of elongation of the trench.
 3. The semiconductor device of claim 1 wherein: the trench-defining layer includes a base sub-layer and a lateral wall sub-layer; the base sub-layer includes a top surface that defines a bottom surface of the trench; the lateral wall sub-layer includes two lateral surfaces that define two upstanding lateral surfaces of the trench; and the base sub-layer and lateral sub-layer are made from different materials.
 4. The semiconductor structure of claim 3 wherein: the material of the base sub-layer allows therefrom epitaxial growth of the material of the epitaxial layer; and the material of the lateral wall sub-layer does not allow therefrom epitaxial growth of the material of the epitaxial layer.
 5. The semiconductor structure of claim 3 wherein the defect-blocking member(s) set is made from the same material as, and is unitary with the lateral wall sub-layer.
 6. The semiconductor structure of claim 3 wherein: the substrate is made from one of the following materials: silicon, SiGe (silicon germanium) or germanium; and the lateral wall sub-layer is made from a dielectric material.
 7. The semiconductor structure of claim 1 wherein the epitaxial layer is made of one of the following materials: a III-V semiconductor material.
 8. The semiconductor structure of claim 1 wherein a top surface of the epitaxial layer and a top surface of the trench-defining layer together form a flat, planar surface.
 9. The semiconductor structure of claim 1 wherein: each defect-blocking member of the defect-blocking member(s) set has a top surface; the epitaxial growth layer has a top surface; and the top surfaces of the defect-blocking member(s) are all below the top surface of the epitaxial layer.
 10. The semiconductor structure of claim 1 wherein the defect-blocking member(s) set are shaped and sized so that the trench includes: (i) a lower tier that follows a zig-zag pattern, and (ii) an upper tier that is free of defect blocking members.
 11. The semiconductor structure of claim 1 wherein the defect-blocking member(s) of the defect-blocking member(s) set alternately extend from opposing lateral walls of the trench.
 12. The semiconductor structure of claim 11 wherein the defect blocking members are shaped as rectangular prisms.
 13. A method of at least partially fabricating a semiconductor device, the method comprising: providing an initial sub-assembly including a trench-defining layer having a top surface; refining the initial sub-assembly into a first trench-cut intermediate sub-assembly by removing material to form an upper tier of a trench extending downward from the top surface of the trench-defining layer, the upper tier of the trench including two lateral trench surfaces and a bottom trench surface; and refining the first trench-cut intermediate sub-assembly into a second trench-cut intermediate sub-assembly by selectively removing material in a downwards direction starting from the bottom surface of the trench to form a lower tier of the trench, with the selective removal of material leaving at least a first defect blocking member in the lower tier of the trench.
 14. The method of claim 13 wherein: the trench-defining layer includes a base sub-layer and a lateral wall sub-layer; and the base sub-layer and lateral sub-layer are made from different materials.
 15. The method of claim 13 wherein: in refining the initial sub-assembly into the first trench-cut intermediate sub-assembly, the material removal is performed by reactive ion etching; and in refining the first trench-cut intermediate sub-assembly into the second trench-cut intermediate sub-assembly, the material removal is performed by reactive ion etching.
 16. The method of claim 13 further comprising: refining the second trench-cut intermediate sub-assembly into an epitaxially-grown intermediate sub-assembly by epitaxially growing an epitaxial layer to fill the lower tier of the trench and at least a portion of the upper tier of the trench.
 17. The method of claim 16 wherein the epitaxial layer is made of a III-V semiconductor material.
 18. The method of claim 16 further comprising: refining the epitaxially-grown intermediate sub-assembly into a planarized intermediate sub-assembly by performing a chemical-mechanical planarization on a top surface of the epitaxially-grown intermediate sub-assembly.
 19. The method of claim 18 further comprising: Refining the planarized intermediate sub-assembly into a finished FET semiconductor device.
 20. A field-effect transistor (FET) device comprising: a FET components set including a first gate and a first contact; trench-defining layer; an epitaxial layer; and a set of defect-blocking member(s) including at least one defect-blocking member; wherein: the epitaxial layer is formed by epitaxial growth; the trench-defining layer includes a trench surface which defines an elongated trench interior space; each defect-blocking member of the set of defect-blocking members extends from the trench surface into the trench interior space; the epitaxial layer is located in the portions of the trench interior space not occupied by the set of defect-blocking member(s); and the FET components set are located at least partially on top of a top surface of the epitaxial layer. 